Quick Coat Dry Coating
Q-Coati is a specialty coating that only Metacylics Coatings manufacturers. This material is great when you need a job done fast. We can apply for up to two passes per day. Cutting the application time nearly in half. If you need your roof coated in a hurry but don’t want to cut corners. We recommend calling Factory Direct Roofing, LLC, for a free estimate using Q-Coat.
Request your Free roof inspection and estimate at pierce@factorydirectroofing.net
Check out these specifications.
DESCRIPTION: WHITE, water-based acrylic elastomeric coating with improved resistance to early light rain, mist, and high humidity. Non-volatile, highly adhesive, UV resistant, reflective, protective coating for almost any surface. USES: For use as a reflective protective coating over BUR Asphalt, T&G, Granulated Cap sheet, Rolled Roofing, Metal, Concrete, Wood, Foam, EPDM, TPO, PVC and Stucco surfaces. When applied with Metacrylics Primer, Base, and Polyester fabric, this product is recommended for all roofs and decks.
- Skin formation through changes in pH
- Acrylic White QS formulations have a 20-minute film set time vs 1 hour or more for other coating products independent of ambient humidity Advantages of Acrylic White QS – Improved resistance to early light rain, mist, and high humidity.
- Adhesion to various roofing substrates
- Very high DPUR
- Surface Cross-Linking Technology
- Hail resistant
- Very high water resistance …with the advantages of Quick Set Technology
- Washout resistance after just a few minutes independent of ambient humidity- Crack Bridging
COLOR: White
ZINC OXIDE: Metacrylics Acrylic White contains no zinc oxide. California Prop. 65 has identified zinc oxide as a hazardous material. No product manufactured by Metacrylics contains zinc oxide. This has been verified by independent testing by ICC-ES and UL Laboratories, our quality control agency.
TITLE 24: Compliant. Cool Roof Rating Council testing: C-1371 Solar Reflectance 0.87 and C-1371 Thermal Emittance 0.90. CRRC Seller ID No: 0660.
LEED POINTS: Available for heat island affect.
USGBC: U.S. Green Building Council member ICC-ES: ICC-Evaluation Services, Inc. listed Report No. 4785 complying with U.S. Building Codes.
UL CLASSIFIED: Quality Control Agency and Class A Fire and Wind Uplift rated.
WEATHERING: 2,000 hours weatherometer – no cracking, crazing, or erosion, slight chalking. ASTM D638
TEMPERATURE CYCLING AND PENETRATION: Tests conducted in accordance with the “Acceptance Criteria for Special Roofing Systems” as published by the International Conference of Building Officials (ICC-ES). Results: PASS. Samples averaged 1.626 before testing. Samples averaged 1.610 after being subjected to the Weatherometer. The change in thickness was less than 1%. Examination of the samples after testing showed no evidence of tearing or cracking of the protective coating.
*Temperature Cycling and Penetration Testing: 25 continuous cycles of 1 hour of water exposure at room temperature prior to 6 hours at -40º F, 2 hours at 70º F, 14 hours at 180º F and 1 hour at 70º F. Spray nozzles delivered 6 in. of water per hour at a temperature of 40º F to 60º F. At the conclusion of the 25 cycles the specimens were examined.
FLASHPOINT: No flash at 200° F (water-based). ASTM 1310, Tag Open Cup
FLEXIBILITY: Low-Temperature Flexibility: pass 1″ :-40° F ASTM C836
TENSILE STRENGTH *Includes Metacrylics Stitch bonded polyester fabric (10 mils)
Strength: 156 psi (81 mils*) Strength at break 1,914 psi 74º F ASTM D412 (10 mils)
ELONGATION: 149% ave(81 mils*)Strength at break 3,540 psi , 0º F ASTM D412
HARDNESS: Shore A 41 ASTM D-676 (8 days cure + 4 hours 120° F)
PERMEABILITY: 0.01 milligrams water loss. Payne Permeability cups.
No Dollar Limit (NDL) Warranty
ROC 336296